|Description||Chile Market Wholesale Customized Champagne Titanium Anodized Aluminum Profile Building Materials|
|Material Thickness(t)||1.0/1.1/1.2/1.4 mm|
|Materiral||aluminum alloy 6063,6063A,6060,6061|
|Color||Silver, Bronze, Champagne, Black, (RAL series)etc.|
|Surface Treatment||anodized, powder coated, electrophoresis, wood grain, polished and etc|
|Shape||Square, Rectangle, Angle, Round, Flat, Oval, and according to customer's drawing.|
|Length||Normal length=6m or in customer's order|
|Usage||Building, Production Line, Decoration, Industrial, Transportation, Door and window, etc.|
1. Pearl cotton foam for each profile;
2. Wrap with shrink film exterior;
3. Packed according to customer request.
Providing colorful products with various mechanical
performances to adapt all kinds of architectural styles
1. Chemical oxidation
At a certain temperature, a thin oxide film is formed on the surface of aluminum alloy profile through chemical reaction, which is called chemical oxidation of aluminum. This method does not need to pass through current, and the process is simpler and cheaper than electrochemical oxidation. The oxide film is very thin, and the film thickness is 0.5~4 μ M or so, the film is soft and has low wear resistance, so it cannot be used alone. The film has good physical adsorption capacity and is a good primer. The protective layer obtained by chemical oxidation can greatly improve the protective ability of parts.
2. Anodic oxidation method
Anodizing of aluminum alloy profile is made by electrolysis in oxalic acid, sulfuric acid and chromic acid aqueous solution with aluminum or aluminum alloy as anode and lead, carbon or stainless steel as cathode. Electro anodic oxidation can obtain film-forming speed that is difficult to obtain by natural oxidation. In the process of oxidation film formation, two processes occur at the same time: one is the formation of Al2O3 oxide film on the surface of aluminum plate; Second, the formation process of oxide film is accompanied by the dissolution of oxide film. Only when the formation rate of the oxide film exceeds its dissolution rate can a certain thickness of the oxide film be obtained, and the thickness of the film is generally 5~15 um. The film is a double-layer structure consisting of a dense barrier layer and a porous layer with a columnar structure. Anodic oxidation films of aluminum alloy profiles can be divided into two categories: porous films formed in acid electrolyzers such as sulfuric acid and oxalic acid, forming micropores perpendicular to the surface; Barrier film is a porous and extremely thin film formed in electrolyte, such as ammonium borate, which is commonly used in electrolytic capacitors.
1. Where you intend to use the aluminium profiles?
2. If you have the estrusion drawing, send us and we develop the correspondence mold.
3. Which color you want or tell us the architectural style you like.
4. Purchase quantity. It will convenient us to give you the best price.