1. Hot water flushing: after oxidation, aluminum parts need to be flushed with hot water in order to aging the film. However, the water temperature and time should be strictly controlled. If the water temperature is too high, the film becomes thinner and the color becomes lighter. The above similar problems will also occur if the treatment time is too long. The appropriate temperature and time are: temperature 40 ~ 50 ℃ and time 0.5 ~ 1min.
2. Drying: it is better to dry naturally. Hang the aluminum parts washed with hot water obliquely on the shelf, so that the free water on the working surface flows downward in a vertical direction. The water drops flowing to the lower corner are absorbed with a towel. The color of the film dried by this method is not affected and appears natural.
3. Aging. The aging method can be determined according to the climatic conditions. In summer with strong sunlight, it can be exposed to the sun. In rainy days or winter, it can be baked in an oven. The process conditions are: temperature 40 ~ 50 ℃, time 10 ~ 15min
4. For the repair of unqualified parts, unqualified conductive oxide film parts should be picked out before drying and aging processes. It is difficult to remove the film after drying and aging, which will affect the surface roughness of aluminum parts. For unqualified workpieces, we can take the following simple measures to solve them: first, clamp the unqualified workpieces on the fixture for aluminum anodizing, and then anodize them according to the anodizing method of aluminum in sulfuric acid solution for 2 ~ 3min. After the film is soft and falls off, the conductive anodizing can be carried out again after a little cleaning with alkaline solution and light emitting with nitric acid.
Description | Black Anidized Aluminum Profiles Aluminium Decorative Aluminum Extrusion For Frame |
Material Thickness(t) | t=0.8-2.0 mm |
Materiral | Aluminum Alloy 6063 |
Annealing Treatment | T3-T8 |
Color | Champagne, Silver White ,Bronze, Grey, Black, (RAL series)etc. |
Surface Treatment | electrophoresis, anodized, wood grain, polished and etc |
Shape | Break Bridge,T Shape,Square, Round, Flat, Oval, and according to customer's drawing. |
Length | Normal length=6m or in customer's order |
Usage | Building, Production Line, Decoration, Industrial, Transportation, Door and window, etc. |
Package |
1. Pearl cotton foam for each profile; 2. Wrap with shrink film exterior; 3. Packed according to customer request. |
Advantages/Features |
Providing colorful products with various mechanical performances to adapt all kinds of architectural styles |
Aluminum or aluminum alloy products are used as anodes in electrolyte solution, and the process of forming aluminum oxide film on the surface of the aluminum and aluminum alloy is called anodic oxidation treatment of aluminum and aluminum alloy. After anodization, the surface of aluminum can produce several microns - hundreds of microns of oxide film. Compared with the natural oxide film of aluminum alloy, its corrosion resistance, wear resistance and decoration have been obviously improved and improved.
- The aluminum oxide film is a porous membrane. Whether it is coloured or not, it must be closed before being put into use, so as to improve its corrosion resistance and weatherability. There are three kinds of treatment methods, namely, high temperature hydration reaction closed, inorganic salt closure and organic matter closure.
(1) High temperature water sealing.
This method utilizes the hydration reaction of aluminum oxide film and water to turn the amorphous membrane into a hydrated crystalline membrane.
The hydration reaction can be carried out at both normal and high temperatures, but at high temperatures, especially at the boiling point, the hydrated crystalline membrane is a very stable and irreversible crystalline film. Therefore, the most commonly used aluminum oxide film is treated by boiling water or steam treatment.
(2) Sealing of inorganic salts.
Inorganic salt method can improve the fastness of organic coloring dyes, so it is often used in chemical coloring.
(3) Organic sealing method.
This is the soaking, soaking or coating of the aluminum oxide film. Because of the high cost and the increase of the process flow, it is not easy to use, more or more of the two kinds of methods mentioned above, and the first kind of high temperature hydration is the mainstream.
Implement National Standard | GB/5237.2-2008 |
Ingot State | Nonferrous mental industrial standard YS67-93 |
Chemical Of Oxide Film | GB/T3190-96 |
Class Of Oxide Film | AA10 , AA15 ,AA20 |
Surface Type | Matte ,Flat |
Colors | Silver , White ,Bronze , Champagne |
Advantage/Features | Corrosion-Resistant , Durable , Shining And Decorative |
1. Where you intend to use the aluminium profiles?
2. If you have the estrusion drawing, send us and we develop the correspondence mold.
3. Which color you want or tell us the architectural style you like.
4. Purchase quantity. It will convenient us to give you the best price.
Contact Us at Any Time